Hydrogen cracking is typically formed at right angles to the stress and is positively identified by its Trans granular appearance when viewed at X – 100 magnifications. In ferritic steels hydrogen which enters the weld metal during welding moves into the HAZ and due to gas forming characteristics and the residual stress, cracking may result.